| The evolution of physical and mechanical properties of concrete specimens under acid corrosion |
| WANG Hui1, HUANG Xin1,2*, JIN Guolong1,3
|
1. Department of Geotechnical Engineering, Tongji University, Shanghai 200092, China;
2. College of Civil Engineering and Architecture, Xinjiang University, Urumqi 830047, Xinjiang, China;
3. China Shipbuilding NDRI Engineering Co., Ltd., Shanghai 200063, China |
|
|
|
|
Abstract In order to analyze the influence of sulfuric acid corrosion on the mechanical properties of the deep water storage and sewage tunnel lining structure(short for “deep tunnel”), this research carried out sulfuric acid corrosion tests with initial pH=1 on the standard concrete specimens with a steel fiber volume ratio of 0% and 1%, and considered two corrosion conditions of single-face and all-face immersion. The surface pH value, mass change rate, uniaxial compressive strength and reaction products of concrete specimens under different corrosion time were systematically analyzed. The results showed that the concrete's strength changed nonlinearly with corrosion time. Because the addition of steel fiber resists the diffusion of sulfuric acid, the reaction process in the early stage of corrosion was slowed down and the reaction products were reduced. Therefore, the strength and quality of steel fiber concrete under acid corrosion immersion did not change as rapidly as that of plain concrete under the same condition. The mass increase rate of concrete specimens under all-face immersion was greater than that of specimens soaked on one side under the same conditions. Combined with XRD analysis, it could be seen that gypsum was formed after reaction. The contact area between all-face corrosion and sulfuric acid was larger, so the reaction products were generated faster, and the corresponding strength and mass increase were also faster.
|
|
Received: 02 September 2023
Published: 19 December 2023
|
|
|
|
|
| [1] |
高始军. 超大直径长距离跨海高铁盾构隧道——广湛铁路湛江湾海底隧道项目介绍[J]. 隧道与地下工程灾害防治, 2021, 3(4): 91-94. GAO Shijun. Super-large diameter and long-distance cross-sea high-speed rail shield tunnel—introduction of Zhanjiang Bay Subsea Tunnel Project of Guangzhou-Zhanjiang Railway[J]. Hazard Control in Tunnelling and Underground Engineering, 2021, 3(4): 91-94.
|
| [2] |
宋嘉美, 高祯, 杨园晶,等. 深圳市前海——南山排水深隧系统工程设计[J]. 中国给水排水, 2021, 37(18): 76-81. SONG Jiamei, GAO Zhen, YANG Yuanjing, et al. Design of Qianhai-Nanshan deep tunnel drainage system in Shenzhen[J]. China Water & Wastewater, 2021, 37(18): 76-81.
|
| [3] |
王晓鹏. 苏州河深隧调蓄工程试验段建造管理关键技术[J]. 中国市政工程, 2022(3): 30-32. WANG Xiaopeng. Key technologies for construction management of Suzhou Creek Deep Tunnel Regulation & Storage Project test section[J]. China Municipal Engineering, 2022(3): 30-32.
|
| [4] |
宋战平, 刘彦龙, 张玉伟. 黄土隧道深浅埋界限划分研究现状及展望[J]. 隧道与地下工程灾害防治, 2021, 3(2): 1-15. SONG Zhanping, LIU Yanlong, ZHANG Yuwei. Research and prospect of demarcation of deep and shallow buried in loess tunnel[J]. Hazard Control in Tunnelling and Underground Engineering, 2021, 3(2): 1-15.
|
| [5] |
YUAN H F, DANGLA P, CHATELLIER P, et al. Degradation modelling of concrete submitted to sulfuric acid attack[J]. Cement and Concrete Research, 2013, 53: 267-277.
|
| [6] |
刘江林. 酸雨环境下混凝土宏细观受压性能试验研究[D]. 大连: 大连海事大学, 2009. LIU Jianglin. Experimental study on macro-meso compressive property of concrete exposed to simulated acid rain environment[D].Dalian: Dalian Maritime University, 2009.
|
| [7] |
强跃, 李莉, 何泽平. 钢纤维混凝土抗酸性腐蚀环境的试验研究[J]. 混凝土, 2011(6): 41-42. QIANG Yue, LI Li, HE Zeping. Test research on the steel fiber reinforced concrete against the acid environment[J]. Concrete, 2011(6): 41-42.
|
| [8] |
杨凯. 酸性水腐蚀下混凝土性能的劣化与防腐技术研究[D]. 武汉: 武汉理工大学, 2011. YANG Kai. Research on properties deterioration and corrosion prevention technology of concrete in acidic water[D].Wuhan: Wuhan University of Technology, 2011.
|
| [9] |
李北星, 周长泉, 蔡老虎, 等. 硫酸环境作用下粉煤灰混凝土性能劣化时变规律[J]. 材料科学与工程学报, 2014, 32(6): 809-815. LI Beixing, ZHOU Changquan, CAI Laohu, et al. Time-dependent rules of performance degradation of fly ash concretes in sulfuric acid environments[J]. Journal of Materials Science and Engineering, 2014, 32(6): 809-815.
|
| [10] |
曾晓辉, 杨凯, 王平,等. 模拟酸雨对板式无砟轨道CA砂浆的侵蚀破坏机理[J]. 建筑材料学报, 2016, 19(3): 472-478. ZENG Xiaohui, YANG Kai, WANG Ping, et al. Erosion damage mechanism of CA mortar in slab ballastless track under simulating acid rain[J]. Journal of Building Materials, 2016, 19(3): 472-478.
|
| [11] |
XIAO J, QU W J, LI W G, et al. Investigation on effect of aggregate on three non-destructive testing properties of concrete subjected to sulfuric acid attack[J]. Construction and Building Materials, 2016,115:486-495.
|
| [12] |
阴琪翔, 侯明姣, 杜健民,等. 硫酸溶液中混凝土的腐蚀速率研究[J]. 混凝土, 2017(11): 74-76. YIN Qixiang, HOU Mingjiao, DU Jianmin, et al. Research on the corrosion rate of concrete under sulfuric acid solution[J]. Concrete, 2017(11): 74-76.
|
| [13] |
阴琪翔, 侯明姣, 杜健民,等. 硫酸溶液中水灰比对混凝土腐蚀速率影响研究[J]. 混凝土, 2018(1):61-63. YIN Qixiang, HOU Mingjiao, DU Jianmin, et al. Research of water to ash ratio on the corrosion rate of concrete under sulfuric acid solution[J]. Concrete, 2018(1):61-63.
|
| [14] |
王海柱. 酸性腐蚀环境中纤维混凝土耐久性退化的试验研究[D].杭州: 浙江工业大学, 2018. WANG Haizhu. An experimental study on the deterioration of properties of fiber-reinforced concrete in acid corrosive environments[D]. Hangzhou: Zhejiang University of Technology, 2018.
|
| [15] |
KHAN H A, CASTEL A, KHAN M S H, et al. Durability of calcium aluminate and sulphate resistant Portland cement based mortars in aggressive sewer environment and sulphuric acid[J]. Cement and Concrete Research, 2019, 124:105852.
|
| [16] |
闻宝联. 城市污水环境下混凝土腐蚀及耐久性研究[D]. 天津: 天津大学, 2005. WEN Baolian. The study on corrosion and durability of concrete in municipal sewerage[D].Tianjin: Tianjin University, 2005.
|
|
|
|